Characterization of sodium cobalt oxides related to PB-phase superconductor

Chemistry of Materials
  • Kazunori Takada
  • ,
  • Minoru Osada
  • ,
  • Fujio Izumi
  • ,
  • Hiroya Sakurai
  • ,
  • Eiji Takayama-Muromachi
  • ,
  • Takayoshi Sasaki

17
開始ページ
2034
終了ページ
2040
DOI
10.1021/cm047737y

This paper reports characterization of sodium cobalt oxides related to a PS-phase superconductor (space group R3̄m) newly found other than P2 phase (space group P63/mmc). α-NaCoO2 used as a parent compound for the synthesis of the superconductor was oxidized to be Na 0.42CoO2, in which the rhombohedral structure in the parent phase providing octahedral coordination environment for Na+ ions changed to a monoclinic lattice with trigonal prismatic sites. Hydration of the as-oxidized Na0.42CoO2 to the superconducting bilayer-hydrate phase was accompanied by the ion exchange between Na+ and H3O+ ions and reductive insertion of H 3O+ ions as observed in the formation of P2-phase superconductor. Partial dehydration of the superconducting phase transformed its bilayer-hydrate structure into a monolayer-hydrate one, in which the superconductivity disappeared again. Influence of the decreasing interlayer distance caused by the dehydration upon the guest species is discussed in combination with the results of Raman spectroscopy. © 2005 American Chemical Society.

リンク情報
DOI
https://doi.org/10.1021/cm047737y
Scopus
https://www.scopus.com/record/display.uri?eid=2-s2.0-17744386182&origin=inward
URL
https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=17744386182&origin=inward