Fatigue behavior of age-hardening Cu-6Ni-1.5Si alloys with different grain sizes

Materials Science Forum
  • Masahiro Goto
  • ,
  • Takaei Yamamoto
  • ,
  • Seung Zeon Han
  • ,
  • Junichi Kitamura
  • ,
  • Jee-hyuk Ahn
  • ,
  • Sung Hwan Lim
  • ,
  • Sang-Jun Lee
  • ,
  • Takahito Utsunomiya
  • ,
  • Jehyun Lee

1016
開始ページ
125
終了ページ
131
記述言語
掲載種別
研究論文(学術雑誌)
DOI
10.4028/www.scientific.net/msf.1016.125
出版者・発行元
Trans Tech Publications, Ltd.

On the thermomechanical treatments of Cu-Ni-Si alloy, cold-rolling (CR) before solution heat treatment (SHT) is commonly conducted to eliminate defects in a casting slab. In addition, a rolling is applied to reduce/adjust the thickness of casting slab before SHT. In a heavily deformed microstructure by CR, on the other hand, grain growth during a heating in SHT is likely to occur as the result of recrystallization. In general, tensile strength and fatigue strength tend to decrease with an increase in the grain size. However, the effect of difference in grain sizes produced by with and without CR before SHT on the fatigue strength is unclear. In the present study, fatigue tests of Cu-6Ni-Si alloy smooth specimens with a grain fabricated through different thermomechanical processes were conducted. The fatigue behavior of Cu-Ni-Si alloy was discussed.

リンク情報
DOI
https://doi.org/10.4028/www.scientific.net/msf.1016.125
URL
https://www.scientific.net/MSF.1016.125.pdf
ID情報
  • DOI : 10.4028/www.scientific.net/msf.1016.125
  • eISSN : 1662-9752

エクスポート
BibTeX RIS