Kyropoulos growth of a 300 g SrB4O7 single crystal using a twin-type stirring blade
Japanese Journal of Applied Physics
- ,
- ,
- ,
- ,
- ,
- ,
- ,
- ,
- 巻
- 61
- 号
- 7
- 開始ページ
- 075503
- 終了ページ
- 075503
- 記述言語
- 掲載種別
- 研究論文(学術雑誌)
- DOI
- 10.35848/1347-4065/ac6f35
- 出版者・発行元
- IOP Publishing
Abstract
We report the successful Kyropoulos growth of a large strontium tetraborate (SrB4O7, SBO) single crystal that weighs more than 300 g. In order to grow the large and transparent crystal, a new twin-type stirring blade was used along with a 150 mm diameter crucible. The use of the stirring blade results in the production of the world’s largest SBO crystal with dimensions of 100 mm (a) ×30 mm (b) ×32 mm (c), a weight of 328.2 g, and wide transparency down to 130 nm. These results will then lead to the development of large SBO crystals as optical window materials for high-power DUV laser processing systems.
We report the successful Kyropoulos growth of a large strontium tetraborate (SrB4O7, SBO) single crystal that weighs more than 300 g. In order to grow the large and transparent crystal, a new twin-type stirring blade was used along with a 150 mm diameter crucible. The use of the stirring blade results in the production of the world’s largest SBO crystal with dimensions of 100 mm (a) ×30 mm (b) ×32 mm (c), a weight of 328.2 g, and wide transparency down to 130 nm. These results will then lead to the development of large SBO crystals as optical window materials for high-power DUV laser processing systems.
- リンク情報
- ID情報
-
- DOI : 10.35848/1347-4065/ac6f35
- ISSN : 0021-4922
- eISSN : 1347-4065