透過電子顕微鏡による Li2NH の水素化反応機構の検討
日本金屬學會誌
- ,
- ,
- ,
- ,
- ,
- ,
- ,
- 巻
- 77
- 号
- 12
- 開始ページ
- 571
- 終了ページ
- 574
- 記述言語
- 日本語
- 掲載種別
- DOI
- 10.2320/jinstmet.JC201307
- 出版者・発行元
- The Japan Institute of Metals
In order to clarify the reaction mechanism of the hydrogenation process in the Li2NH system, we have observed the partially hydrogenated samples by transmission electron microscopy (TEM). From the TEM images of partially hydrogenated samples, it was shown that the LiNH2 phase was located between Li2NH phase, which was almost at the center of the particle, and LiH particles with the size of 100 nm. This result indicated that LiH was generated and grew up at the outside of the complex particle of Li2NH and LiNH2 with Li moving from the center to the surface of the particle.