Morphology of four kinds of aromatic polyimidazoles was examined by using reaction-induced crystallization during solution polymerization at a concentration of 1% at 350 degrees C in liquid paraffin (LPF), dibenzyltoluene (DBT), and the mixture of these solvents. Aggregates of ribbon-like crystals of poly[2,6-(2,6-naphthalene)-benzobisimidazole] were obtained in LPF, and those of plate-like crystals were obtained in DBT/LPF-50 and in DBT. In contrast to this, the network structures of poly[2,2'-(2,6-naphthalene)-5,5'-bibenzimidazole)] (PNT-BBI) nanofibers with the diameter of 25 to 90 nm was mainly obtained in DBT. The network structures of the PNT-BBI nanofibers could be recognized as nonwoven fabrics of the high-performance polymers. Imidazole trimers were precipitated to form the ribbon-like crystals and then they were continuously supplied from solution to grow the crystals. Molecular weight increased by the polymerization on the surface of the crystals when they crystallized and in the crystals. The initially formed aggregates of ribbon-like crystals changed to the nanofibers with time. In the case of poly[2,6-(4,4'-biphenylene)-benzobisimidazole] and poly[2,2'-(4,4'-biphenylene)-5,5'-bibenzimidazole)], they exhibited various morphologies such as spheres, lath-like crystals, and the spherical aggregates of lath-like crystals depending on the solvent, but fibers like PNT-BBI were not formed. The crystals obtained in this study possessed very high crystallinity and the outstanding thermal stability measured by TGA. (C) 2011 Wiley Periodicals, Inc. J Appl Polym Sci 121: 2851-2860, 2011