The substrate-film lattice mismatch in La0.7Ba0.3MnO3 thin films for uncooled infrared bolometric applications

IEEJ Transactions on Sensors and Micromachines
  • Ken-ichi Hayashi
  • ,
  • Eiji Ohta
  • ,
  • Hideo Wada

121
10
開始ページ
542
終了ページ
547
記述言語
英語
掲載種別
研究論文(学術雑誌)
DOI
10.1541/ieejsmas.121.542

La0.7Ba0.3MnO3 (LBMO) thin films known to colossal magnetoresistance were deposited for uncooled infrared bolometers. The optimum oxygen pressure was examined in the process of the laser ablated LBMO films, and films were deposited on SrTiO2 (100), LaAIO2 (100) and MgO (100) substrates under the optimum oxygen pressure. The lattice mismatch between these substrates and LBMO films changed the surface structure of films. In X-ray diffraction and atomic force microscope, the LBMO film deposited on SrTiO3 (the LBMO/STO film) showed a high orientation for the substrate, and the grain growth of the LBMO/STO film was progressed. The temperature dependence of resistivity has a good agreement with that of LBMO bulk. In the near-room temperature, the LBMO/STO film showed a high TCR value, about 4 %/K. Moreover, TCR values of the LBMO/STO film were over 2 %/K from 300K to 335K. On the other hand, LBMO films deposited on LaAlO: and MgO substrates, having large substrate-film lattice mismatches, showed a low TCR value, below 2%/K, in the near-room temperature. © 2001, The Institute of Electrical Engineers of Japan. All rights reserved.

リンク情報
DOI
https://doi.org/10.1541/ieejsmas.121.542
Scopus
https://www.scopus.com/inward/record.uri?partnerID=HzOxMe3b&scp=85024470988&origin=inward 本文へのリンクあり
Scopus Citedby
https://www.scopus.com/inward/citedby.uri?partnerID=HzOxMe3b&scp=85024470988&origin=inward
ID情報
  • DOI : 10.1541/ieejsmas.121.542
  • ISSN : 1347-5525
  • ISSN : 1341-8939
  • eISSN : 1347-5525
  • SCOPUS ID : 85024470988

エクスポート
BibTeX RIS