The Effect of Annealing Temperature on Tensile Properties in a Fine-Grained Fe(3)Al-Based Alloy Containing kappa-Fe(3)AlC Carbide Particles
ADVANCED INTERMETALLIC-BASED ALLOYS FOR EXTREME ENVIRONMENT AND ENERGY APPLICATIONS
- ,
- ,
- 巻
- 1128
- 号
- 開始ページ
- 191
- 終了ページ
- 196
- 記述言語
- 英語
- 掲載種別
- 出版者・発行元
- MATERIALS RESEARCH SOCIETY
The effect of annealing temperature on the room temperature tensile properties was investigated in a fine-grained Fe(3)Al based-alloy, and the correlation between microstructure, texture and tensile properties is discussed. Tensile elongation showed a peak as a function of annealing temperature. The highest elongation was obtained in the recrystallized samples annealed at 700 degrees C. The decrease in the elongation with increasing annealing temperature above 700 degrees C is attributed to the increase in the fraction of < 100 > oriented grains with respect to the tensile direction. A high sensitivity to environmental embrittlement was observed in the partially recrystallized samples annealed at 650 degrees C.
- リンク情報
- ID情報
-
- ISSN : 0272-9172
- Web of Science ID : WOS:000271831400029