Effect of Si3N4 addition on the mechanical properties, microstructures, and wear resistance of Ti-6Al-4V alloy
JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
- ,
- ,
- ,
- 巻
- 23
- 号
- 2
- 開始ページ
- 257
- 終了ページ
- 261
- 記述言語
- 英語
- 掲載種別
- 研究論文(学術雑誌)
- 出版者・発行元
- JOURNAL MATER SCI TECHNOL
In order to improve the wear resistance of Ti-6Al-4V, different amounts of Si3N4 powder were added into the alloy powder and sintered at 1250 C. Porous titanium alloy with higher wear resistance was successfully fabricated. At sintering temperature, reaction took place and a new hard phase of Ti5Si3 formed. The mechanical properties of the fabricated alloys with different amounts of Si3N4 addition were investigated. The hardness of Ti-6Al-4V, which is the index of wear resistance, was increased by the addition of Si3N4. Amounts of Si3N4 addition have very significant influences on hardness and compressive strength. In present study, titanium alloy with 5 wt pct Si3N4 addition has 62% microhardness and 45% overall bulk hardness increase, respectively. In contrast, it has a 16.4% strength reduction. Wear resistance was evaluated by the weight loss during wear test. A new phase of Ti5Si3 was detected by electron probe microanalyzer (EPMA) and X-ray diffraction (XRD) method. The original Si3N4 decomposed during sintering and transformed into titanium silicide. Porous structure was achieved due to the sintering reaction.
- リンク情報
- ID情報
-
- ISSN : 1005-0302
- Web of Science ID : WOS:000245602100018