- JAPAN INST METALS
Commercially pure titanium plates were embedded in mixtures of steel and activated carbon powders and then heated at 1273 K for 3.6 ks in a nitrogen flow. During this simplified treatment, a Ti(C, N) layer with a thickness of approximately 10 mu m formed on the titanium surface. The surface hardness of the titanium plates coated with the Ti(C, N) layer was more than HV = 1000 regardless of the steel powder ratio in the mixture. Although a Ti(C, N) layer formed upon heat treatment with the activated carbon powder alone, addition of the steel powder led to an increase in the surface hardness and layer thickness. From X-ray diffraction results, Ti(C, N) began to form on the titanium plate heat-treated at 1073 K and became a complete layer at higher heating temperatures. Instead of activated carbon, the use of graphite with added alumina as a reliable anti-sintering agent had no negative effects on the formation of the Ti(C, N) layer.
Web of Science ® 被引用回数 : 5
Web of Science ® の 関連論文(Related Records®)ビュー
- DOI : 10.2320/matertrans.M2012409
- ISSN : 1345-9678
- eISSN : 1347-5320
- Web of Science ID : WOS:000325122900037