Aluminizing of High-carbon Steel by Explosive Welding and Subsequent Heat Treatment

ISIJ INTERNATIONAL
  • Yasuhiro Morizono
  • ,
  • Takuya Yamaguchi
  • ,
  • Sadahiro Tsurekawa

55
1
開始ページ
272
終了ページ
277
記述言語
英語
掲載種別
研究論文(学術雑誌)
DOI
10.2355/isijinternational.55.272
出版者・発行元
IRON STEEL INST JAPAN KEIDANREN KAIKAN

A carbon steel plate containing 0.87 mass% C was coated with an aluminum foil with a thickness of 100 mu m by explosive welding. This aluminum-coated steel was heat-treated in the temperature range of 973-1273 K for up to 7.2 ks in the air to investigate reactions between molten aluminum and high-carbon steel from the viewpoint of aluminide coating. An aluminized layer was basically composed of Fe2Al5, FeAl, Fe3Al containing carbon (Fe3Al(C)), and ferrite stabilized by aluminum diffusion (alpha-Fe(Al)). FeAl2 was detected with Fe2Al5 at heating temperatures of more than 1 223 K, whereas FeAl had two layers due to its chemical composition. In addition, defects like a crack and a void were observed in the vicinity of the FeAl/alpha-Fe(Al) interface after heating at 1 273 K for 3.6 ks. To reduce brittle Fe2Al5 and FeAl2 in the aluminized layer, the steel coated with aluminum with a thickness of 50 mu m was prepared and then heat-treated under the same conditions. At 1 173 K, the region consisting of FeAl, Fe3Al(C), and alpha-Fe(Al) accounted for a large part of the aluminized layer. This aluminized steel was subjected to quenching and tempering on the basis of features of the used bare steel. As a result, the hardness near the surface of the aluminized layer was approximately equal to that of the steel substrate.

Web of Science ® 被引用回数 : 4

リンク情報
DOI
https://doi.org/10.2355/isijinternational.55.272
Web of Science
https://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcAuth=JSTA_CEL&SrcApp=J_Gate_JST&DestLinkType=FullRecord&KeyUT=WOS:000348554500029&DestApp=WOS_CPL
ID情報
  • DOI : 10.2355/isijinternational.55.272
  • ISSN : 0915-1559
  • eISSN : 1347-5460
  • Web of Science ID : WOS:000348554500029

エクスポート
BibTeX RIS