Morphology control of various aromatic polyimides by using phase separation during polymerization
POLYMER
- ,
- ,
- ,
- 巻
- 48
- 号
- 2
- 開始ページ
- 458
- 終了ページ
- 466
- 記述言語
- 英語
- 掲載種別
- 研究論文(学術雑誌)
- DOI
- 10.1016/j.polymer.2006.11.061
- 出版者・発行元
- ELSEVIER SCI LTD
Morphology control of various aromatic polyimides representative as poly(4,4'-oxydiphenylene pyromelliteimide) was examined by using the phase separation during solution polymerization. Polymerizations of aromatic dianhydrides and aromatic diamines to the polyimides were carried out in poor solvents at 240-330 degrees C for 6 h with no stirring. Polymerization concentrations were from 0.25% to 3.0%. The polyimides were obtained as yellow precipitates. Two categorized morphologies were created, which were particles and crystals exhibiting lath-like and plate-like habits. These morphologies of polyimides could be selectively controlled by the polymerization conditions. The higher concentrations, less miscible solvents and lower temperatures were preferable to yield the particles via liquid-liquid phase separation. On the contrary, the lower concentration, miscible solvents and higher temperature were desirable to yield the crystals. The polyimide precipitates showed high crystallinity and possessed excellent thermal stability at which the 10 wt% loss temperatures in N-2 were in the range of 590-694 degrees C. (c) 2006 Elsevier Ltd. All rights reserved.
- リンク情報
- ID情報
-
- DOI : 10.1016/j.polymer.2006.11.061
- ISSN : 0032-3861
- Web of Science ID : WOS:000243804100006