Radiation-induced crosslinking of polyamide11 in the presence of triallylisocyanurate
POLYMER DEGRADATION AND STABILITY
- ,
- ,
- ,
- 巻
- 136
- 号
- 開始ページ
- 98
- 終了ページ
- 102
- 記述言語
- 英語
- 掲載種別
- 研究論文(学術雑誌)
- DOI
- 10.1016/j.polymdegradstab.2016.12.014
- 出版者・発行元
- ELSEVIER SCI LTD
Crosslinking structures were formed in electron beam irradiated polyamidell (PA11) without and with triallyl isocyanurate (TAIC). The gel fractions of PA11 without TAIC steeply increased above the dose of 190 kGy, and saturated to 76.2% at higher than 750 kGy. PA11 was ascertained as a radiation crosslinking type polymer. TAIC was found to promote the induction of crosslinking of PA11 main chains. The network structure of PAD was effectively formed in 3 phr (per hundred resin) TALC at the dose of 10 kGy. The crosslinked PA11 increased the thermal stability, as demonstrated by retention of its original shape at temperatures even higher than 200 degrees C. (C) 2017 Elsevier Ltd. All rights reserved.
- リンク情報
- ID情報
-
- DOI : 10.1016/j.polymdegradstab.2016.12.014
- ISSN : 0141-3910
- eISSN : 1873-2321
- ORCIDのPut Code : 44046521
- Web of Science ID : WOS:000393531300011