Fabrication of c-axis oriented hydroxyapatite ceramics in a rotating high magnetic field using photopolymerization
Journal of the European Ceramic Society
- ,
- 巻
- 40
- 号
- 12
- 開始ページ
- 4332
- 終了ページ
- 4339
- 記述言語
- 掲載種別
- 研究論文(学術雑誌)
- DOI
- 10.1016/j.jeurceramsoc.2020.05.012
C-axis oriented hydroxyapatite (HAp) was prepared by colloidal processing using a photopolymerization reaction in a rotating magnetic field with a UV-curable binder as the solvent. This technique achieved a short processing time of 150 s in a magnetic field as a result of rapid solidification induced by the photopolymerization. The slight difference in refractive index between the HAp material and UV curable resin allowed the fabrication of 1.6 mm thick green compacts. The oriented structure in the compact was maintained from the surface down to a depth of 700 μm, but was randomized at depths of 700 μm and beyond. The orientation degree was retained after sintering at 1250 °C, and the relative density of the compact was approximately 97 %. This technique can be effectively utilized for the manufacture of high-performance biomaterials.
- リンク情報
- ID情報
-
- DOI : 10.1016/j.jeurceramsoc.2020.05.012
- ISSN : 0955-2219
- eISSN : 1873-619X
- SCOPUS ID : 85084994437