Migration behavior of vacancies in electron irradiated Fe-Cu alloys
PHYSICA STATUS SOLIDI C - CURRENT TOPICS IN SOLID STATE PHYSICS, VOL 6, NO 11
- ,
- ,
- ,
- 巻
- 6
- 号
- 11
- 開始ページ
- 2355
- 終了ページ
- 2358
- 記述言語
- 英語
- 掲載種別
- 研究論文(国際会議プロシーディングス)
- DOI
- 10.1002/pssc.200982131
- 出版者・発行元
- WILEY-V C H VERLAG GMBH
The formation of Cu precipiatates in Cu containing steels is one of the key factors leading to embrittlement in reactor pressurer vessel steels. Cu precipitates are formed by the migration of vacancies in steels and the behaviour of these vacancies is therefore important. In the present study, vacancies were introduce into Fe-Cu alloys by electron irradiation with 28 MeV at 100 K. The effects of Cu concentration and tiny Cu precipitates on the migration of vacancies and growth of precipitates in Fe-Cu alloys were investigated by positron annihilation lifetime measurements. The effect of Cu concentration between Fe-0.3 mass% Cu to Fe-0.6 mass% Cu on the migration of vacancies and the formation of Cu precipitates was negligible small. The formation of Cu precipitates was found to decrease the migration temperature of vacancies. (C) 2009 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
- リンク情報
- ID情報
-
- DOI : 10.1002/pssc.200982131
- ISSN : 1862-6351
- Web of Science ID : WOS:000279544900028