Temperature dependence of dislocation bias factors in metals
NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS
- ,
- ,
- 巻
- 267
- 号
- 18
- 開始ページ
- 2971
- 終了ページ
- 2975
- 記述言語
- 英語
- 掲載種別
- 研究論文(学術雑誌)
- DOI
- 10.1016/j.nimb.2009.06.015
- 出版者・発行元
- ELSEVIER SCIENCE BV
Recently, it has been shown that edge dislocations are not stable sinks for vacancies. Trapping and detrapping of vacancies occur as a thermally-activated process. In this paper, the temperature dependence of vacancy absorption coefficient of edge dislocations under irradiation was calculated by using rate equations in Fe and Ni. The temperature dependence was almost the same in both Fe and Ni and did not depend on the damage rate between 10(-10) dpa/s and 10(-6) dpa/s. At low temperatures such as room temperature, the coefficient was low and with increasing irradiation temperatures, it had a peak (500 K) and decreased. (C) 2009 Elsevier B.V. All rights reserved.
- リンク情報
- ID情報
-
- DOI : 10.1016/j.nimb.2009.06.015
- ISSN : 0168-583X
- Web of Science ID : WOS:000271349500003