Preparation of proton-conductive organic-inorganic hybrid titanophosphite membranes
Solid State Ionics
- ,
- ,
- ,
- ,
- ,
- ,
- 巻
- 225
- 号
- 開始ページ
- 232
- 終了ページ
- 235
- 記述言語
- 英語
- 掲載種別
- DOI
- 10.1016/j.ssi.2012.01.040
A novel organic-inorganic hybrid titanophosphite membrane that exhibits proton conductivity at 100-150 °C was successfully prepared. Graded monomer conversion was achieved in the membrane by ultraviolet light (UV) absorption during polymerization: the conversion at the membrane surface was high, whereas that at the inner part was low. As a result, this membrane exhibited water durability as well as a proton conductivity of 6.3 × 10 - 4 S cm - 1 at 150 °C under a N 2 atmosphere. This is because the inner part acted as an acidic site whereas the surface provided water resistance. Thus, the structure of the membrane with graded monomer conversion enables proton conduction under a dry atmosphere at intermediate temperatures. © 2012 Elsevier B.V.
- ID情報
-
- DOI : 10.1016/j.ssi.2012.01.040
- ISSN : 0167-2738
- SCOPUS ID : 84867579449