Mechanical properties and microstructures of cast dental Ti-Fe alloys.
Dental materials journal
- ,
- ,
- ,
- 巻
- 40
- 号
- 1
- 開始ページ
- 61
- 終了ページ
- 67
- 記述言語
- 英語
- 掲載種別
- 研究論文(学術雑誌)
- DOI
- 10.4012/dmj.2019-254
Binary Ti-Fe alloys of varying concentrations of Fe between 5-25% were made, and their castings evaluated in terms of microstructures formed and mechanical properties. The aim of this study was to explore the composition of Ti-Fe alloys that offers improved wear resistance of titanium. X-ray diffraction and microstructural observation revealed that 5-7% Fe, 8-15% Fe, and 20-25% Fe consisted of α+β, single β, and β+TiFe phases, respectively. The hardness of alloys with 8-13% Fe was almost equal to that of Co-Cr alloys but lower than of the other Ti-Fe alloys. Elongation of the Ti-Fe alloys was negligible. However, dimples were observed in specimen containing 7-11% Fe. Alloys with 9% Fe demonstrated the highest strength of more than 850 MPa. We believe that Ti-Fe alloys with 8-11% Fe may be applicable in development of an alloy with good wear resistance due to the exhibited properties of high hardness and ductility albeit low.
- ID情報
-
- DOI : 10.4012/dmj.2019-254
- PubMed ID : 32848101