Graphite surfaces were irradiated by argon (Ar+) ions at 1 key with a simultaneous cobalt (Co) supply at room temperature. Various kinds of carbon nanocomposites, such as nanocones with and without single nanofibers on their tops, nanorods and fish-scale-like nanoprotrusions, were formed depending on Co supply rates. It has been observed that with increasing the Co supply rate the formation of nanoprotrusions without nanofibers became prominent. Both nanofibers and nanoprotrusions were surely composed of carbon and Co, as confirmed by energy-dispersive X-ray analysis. The cobalt carbon nanocomposite fibers (CCNFs), similar to 1.5 mu m in average length, were grown on the top of the nanocones at the Co supply rate of 1.0 nm/min. The field electron emission characteristics of CCNFs thus grown indicated that there is an optimum parameter for the CCNF growth to achieve the better emission performance than that of pristine Ar+-induced carbon nanofibers.